Cone 06 oxidation (first image): Speckled Green Thumb is a heavily pigmented, viscous Stroke & Coat® glaze with black specks that can be used for brush strokes or opaque coverage. One coat will create a translucent finish with subsequent coats adding opacity. We suggest two to three coats for full opacity and all over coverage. Will fire to a gloss finish without clear glaze.
Cone 6 oxidation (second image): Opaque. No color change.
Cone 10 reduction (third image)
Cone 06 oxidation (first image): Speckled Cotton Tail is a heavily pigmented, viscous Stroke & Coat® glaze with yellow, orange and blue specks that can be used for brush strokes or opaque coverage. One coat will create a translucent finish with subsequent coats adding opacity. We suggest two to three coats for full opacity and all over coverage. Will fire to a gloss finish without clear glaze.
Cone 6 oxidation (second image): Opaque. Specks blur and slightly bleed.
Cone 10 Reduction (third image)
Cone 06 oxidation (first image): Speckled Tuxedo is a heavily pigmented, viscous Stroke & Coat® glaze with white specks that can be used for brush strokes or opaque coverage. One coat will create a translucent finish with subsequent coats adding opacity. We suggest two to three coats for full opacity and all over coverage. Will fire to a gloss finish without clear glaze.
Cone 6 oxidation (second image): Opaque. Color slightly Darkens.
Cone 10 reduction (third image)
Cone 06 oxidation (first image): Speckled Grapel is a heavily pigmented, viscous Stroke & Coat® glaze with blue specks that can be used for brush strokes or opaque coverage. One coat will create a translucent finish with subsequent coats adding opacity. We suggest two to three coats for full opacity and all over coverage. Will fire to a gloss finish without clear glaze.
Cone 6 oxidation (second image): Transparent. Color Slightly lightens. Specks bleed.
Cone 10 reduction (third image)
Cone 06 oxidation (first image): Speckled Moody Blue is a heavily pigmented, viscous Stroke & Coat® glaze with white specks that can be used for brush strokes or opaque coverage. One coat will create a translucent finish with subsequent coats adding opacity. We suggest two to three coats for full opacity and all over coverage. Will fire to a gloss finish without clear glaze.
Cone 6 oxidation (second image): Opaque. Color lightens to medium brown. Specks remain.
Cone 10 Reduction (third image)
Cone 06 oxidation (first image): Speckled Teal Next Time is a heavily pigmented, viscous Stroke & Coat® glaze with white specks that can be used for brush strokes or opaque coverage. One coat will create a translucent finish with subsequent coats adding opacity. We suggest two to three coats for full opacity and all over coverage. Will fire to a gloss finish without clear glaze.
Cone 6 oxidation (second image): Opaque. No color change.
Cone 10 reduction (third image)
Cone 06 oxidation (first image): Speckled Jaded is a heavily pigmented, viscous Stroke & Coat® glaze with yellow, orange and blue specks that can be used for brush strokes or opaque coverage. One coat will create a translucent finish with subsequent coats adding opacity. We suggest two to three coats for full opacity and all over coverage. Will fire to a gloss finish without clear glaze.
Cone 6 oxidation (second image): Opaque. Color lightens to medium brown. Specks remain.
Cone 10 reduction (third image)
Cone 06 oxidation (first image): Speckled Pink-A-Boo is a heavily pigmented, viscous Stroke & Coat® glaze with maroon specks that can be used for brush strokes or opaque coverage. One coat will create a translucent finish with subsequent coats adding opacity. We suggest two to three coats for full opacity and all over coverage. Will fire to a gloss finish without clear glaze.
Cone 6 oxidation (second image): Semi-Transparent. Color slightly lightens. Specks bleed.
Cone 10 Reduction (third image)
Composition and Reference Numbers for Mason Stain 6126 Hazelnut Brown COMPOSITION: Al Cr Fe Zn -- REFERENCE NUMBERS: 3, 7
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Composition and Reference Numbers for Mason Stain 6485 Titanium Yellow COMPOSITION: Cr Sb Ti -- REFERENCE NUMBERS: 1a, 3
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Composition and Reference Numbers for Mason Stain 6109 Deep Brown COMPOSITION: Al Cr Fe Zn -- REFERENCE NUMBERS: 3, 6, 7
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Saturated color, dependability, and versatility make Velvets as popular for professionals as they are for children. Velvets fire true-to-color as a Cone 05/06 underglaze or fired to Cone 6. Some colors remain true as high as Cone 10. Try two finish possibilities: When left unglazed these colors have the rich textural appearance of velvet; when covered with AMACO Clear Transparent Matte or Clear Gloss they intensify in color. Can be easily applied to wet clay, greenware, or mature Cone 04 bisque (1971℉ / 1077℃) Saturated Color Apply to unfired clay or bisque True to color Can be used with or without glaze- Food Safe with proper glaze. Cone 05 to 10 Sprayable
Composition and Reference Numbers for Mason Stain 6650 Cobalt-free Black COMPOSITION: Cr Fe -- REFERENCE NUMBERS: 3, 5
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Composition and Reference Numbers for Mason Stain 6223 Ivy Green COMPOSITION: Al, Cr, Si -- REFERENCE NUMBERS: 3, 5
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Cone 06: Use this versatile product to create green fine detail with lines, dots, and letters. Cone 6: No color change. TIP: If applying a clear glaze, use SW-004 Zinc Free Clear for cone 6.
Composition and Reference Numbers for Mason Stain 6306 Vivid Blue COMPOSITION: Al Co Si Zn -- REFERENCE NUMBERS: 1, 3, 6
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Expensive but worth the price. A smooth, not glossy, surface of maroon and green that provides great patterns with reduction. Not fluid. Apply to medium thickness.
Composition and Reference Numbers for Mason Stain 6666 Cobalt-free Black COMPOSITION: Cr Fe Mn -- REFERENCE NUMBERS: 3, 5
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Composition and Reference Numbers for Mason Stain 6202 Florentine Green *discontinued* COMPOSITION: Co Cr Si -- REFERENCE NUMBERS: 1, 3, 6, 8
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Composition and Reference Numbers for Mason Stain 6246 Blue Green COMPOSITION: Co Cr Si Sn Zn -- REFERENCE NUMBERS: 3, 6, 8
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Composition and Reference Numbers for Mason Stain 6500 Sage Grey COMPOSITION: Co Cr Ni Si -- REFERENCE NUMBERS: 1, 3, 6
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Saturated color, dependability, and versatility make Velvets as popular for professionals as they are for children. Velvets fire true-to-color as a Cone 05/06 underglaze or fired to Cone 6. Some colors remain true as high as Cone 10. Try two finish possibilities: When left unglazed these colors have the rich textural appearance of velvet; when covered with AMACO Clear Transparent Matte or Clear Gloss they intensify in color. Can be easily applied to wet clay, greenware, or mature Cone 04 bisque (1971℉ / 1077℃) Saturated Color Apply to unfired clay or bisque True to color Can be used with or without glaze- Food Safe with proper glaze. Cone 05 to 10 Sprayable
Saturated color, dependability, and versatility make Velvets as popular for professionals as they are for children. Velvets fire true-to-color as a Cone 05/06 underglaze or fired to Cone 6. Some colors remain true as high as Cone 10. Try two finish possibilities: When left unglazed these colors have the rich textural appearance of velvet; when covered with AMACO Clear Transparent Matte or Clear Gloss they intensify in color. Can be easily applied to wet clay, greenware, or mature Cone 04 bisque (1971℉ / 1077℃) Saturated Color Apply to unfired clay or bisque True to color Can be used with or without glaze- Food Safe with proper glaze. Cone 05 to 10 Sprayable
Composition and Reference Numbers for Mason Stain 6591 Gun Metal COMPOSITION: Co Ni Zr -- REFERENCE NUMBERS: 3, 6
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide
Composition and Reference Numbers for Mason Stain 6376 Robin's Egg Blue COMPOSITION: Si V Zr -- REFERENCE NUMBERS: 1, 3, 6
REFERENCE CHART 1 Can be used as a body stain at high temperatures. 1a Use as a body stain only. 2 Maximum temperature - 2156° F. 3 Maximum temperature - 2300° F. 4 Maximum temperature - 1976° F. 5 Do not use zinc in glaze. 6 May be used with or without zinc. 7 Zinc not necessary, but gives better results. 8 Best results with no zinc. 9 Glaze must contain 12% to 15% calcium carbonate. COMPOSITION CHART Al Aluminum oxide B Boric oxide Ca Calcium carbonate Cd Cadmium Co Cobalt oxide Cr Chromium oxide Fe Iron oxide Mn Manganese dioxide Ni Nickel oxide Pr Praseodymium oxide Sb Antimony oxide Si Silicon dioxide Sn Tin dioxide Ti Titanium oxide V Vanadium Zn Zinc oxide Zr Zirconium dioxide